Double coated tapes
General-purpose double coated tapes
High-performance, general-purpose double coated series usable for various purposes.
-
- Product name
- T4000/T4000B
-
- Features
-
- High heat resistance for wide ranging applications.
- High adhesion to various type of metal part and plastics.
Safety Data Sheet (SDS) Download
Related articles
Structure
Specifications
| Product name | T4000 (T4000B) |
|---|---|
| Main component | Acrylic base |
| Carrier | Tissue paper |
| Color | Translucent (black) |
| Adhesive thickness(µm) | About 150 |
| Release paper thickness(µm) |
About 150 |
| Bonding strength(N/20mm) ＊ | 11.77 |
| St'd size(width & length) | 500mm x 50m |
| Warranty period from manufacturing date | 12 months |
- UL certificated. UL file No:( UL969 No.MH15431)
＊ 180°peeling strength
Suitable for bonding name plates of metals and plastics.
1.Bonding strength on various type of substrate (180° peeling)
Test Piece Condition
Tape width:20mm
Bonding condition:One stroke with 2-kg roller
Measuring condition:23°C±5°C 60%±20%RH
Peeling speed:300mm/min
Backing material:25µm PET
[Left at RT for one hour before measurement]
Results
(N/20mm)
| 180° peeling strength | Product name | Substrate | ||||||
|---|---|---|---|---|---|---|---|---|
| SUS | AL | ABS | Acrylic | PC | CR | NR | ||
| T4000 | 14.2 | 13 | 14.1 | 14.9 | 15.4 | 3.2 | 2.8 | |
2.Holding power at different temperatures
Test Piece Condition
Substrate:Stainless steel plate (SUS304)
Bonding area:25mm x 25mm
Bonding condition:One stroke with 2-kg roller
[Left at RT for one hour and then at each temperature for 30 minutes before measurement]
[Creep length after one-hour application of 1-kg load]
Results
| Creep length(mm) | Product name | Measurement temperature | ||
|---|---|---|---|---|
| 40°C | 60°C | 80°C | ||
| T4000 | 0.3 | 0.4 | 0.4 | |
3.Reliability of bonding strength at 70° temperatures(180° peeling)
Test Piece Condition
Substrate:Stainless steel plate (SUS304)
Tape width:20mm
Bonding condition:One stroke with 2-kg roller
Peeling speed:300mm/min
Backing material:25µm PET
[Left at RT for one hour and aging at 70°C condition]
Results
4.Bonding strength at different temperatures (180° peeling)
Test Piece Condition
Substrate:Stainless steel plate (SUS304)
Tape width:20mm
Bonding condition:One stroke with 2-kg roller
Peeling speed:300mm/min
Backing material:25µm PET
[Left at RT for one hour and then at each temperature for 30 minutes before measurement]
Results
caution
Note on the characteristic data given - Data on the characteristics of the products described in this page based on the results of evaluations carried out by the company. This does not guarantee that the characteristics of the product conform with your usage environment. Before use, review the usage conditions based on evaluation data obtained from the equipment and substrates actually used.