Single coated tapes

Silicone base adhesive single coated tapes

Special silicone base adhesive coated. Removable.

  • Product name
  • Features
    • Most suitable as splicing tape for (silicone base) release paper, plastic film, and metal foil.
    • Stable bonding performance under a wide range of temperature environments, from low to high temperatures.
    • Offers removable performance with minimal adhesive residue on the substrate.



Product name T4082S
Main component Silicone base
Carrier About 38µm PET
Color Light blue
Adhesive thickness(µm) About 70
Release paper thickness(µm) -
Bonding strength(N/20mm) *1 6
St'd size(width & length) 18mm x 50m
Warranty period from manufacturing date 12 months
  • *1 180° peeling strength

Ideal for bonding difficult-to-bond materials such as silicone rubber and silicone foam; temporary fixing of covers for audiovisual products and computers.

1.Reliability of bonding strength after adhesion under different conditions (180° peeling)

Test Piece Condition

Substrate:Stainless steel plate (SUS304)
Tape width:20mm
Bonding condition:One stroke with 2-kg roller
Measuring condition:23°C±5°C 60%±20%RH
Peeling speed:300mm/min

[Left at RT for one hour and aged under each test condition before measurement]



180° peeling strength Product name Measurement condition Bonding strength
T4082S Initial 6
60°C 95%RH, after 8 hours 6
40°C, after 8 hours 6

2.Holding power at different temperatures

Test Piece Condition

Substrate:Stainless steel plate (SUS304)
Tape width:25mm x 25mm
Bonding condition:One stroke with 2-kg roller
Backing material:25µm PET

[Left at RT for one hour and then at each temperature for 30 minutes before measurement]
[Creep length after one hour application of 1-kg load]



Creep length (mm) Product name Measurement temperature
T4082S 40°C 100°C
0 0


Note on the characteristic data given - Data on the characteristics of the products described in this page based on the results of evaluations carried out by the company. This does not guarantee that the characteristics of the product conform with your usage environment. Before use, review the usage conditions based on evaluation data obtained from the equipment and substrates actually used.