Double coated tapes

Repulsion resistance type double coated tapes

Ideal for 3D curved surface due to excellent static load resistance.

  • Product name
  • Features
    • No solvent used at coating process. UV curable manufacturing method.
    • Excellent static load resistance ; excellent adhesion to curved surfaces and good performance against constant load.
    • Suitable for a wide range of substrates from plastics to metals.
    • PET carrier for excellent handling and punching process.

Product Lineup



Product name G9951-200
Main component Acrylic base
Carrier About 25µm PET
Color Transparent
Adhesive thickness(µm) About 200
Release film thickness(µm) About 50
Bonding strength(N/20mm) *1 15
St'd size(width & length) 500mm x 100m
Warranty period from manufacturing date 12 months
  • *1180° peeling strength

Ideal for bonding plastics, metals, mesh, and cushioning materials used in mobile devices.

1.Bonding strength on various type of substrate (180°, 90° peeling)

Test Piece Condition
Tape width:20mm
Bonding condition:One stroke with 2-kg roller
Measuring condition:23°C±5°C 60%±20%RH
Peeling speed:300mm/min
Backing material:25µm PET

[Left at RT for one hour before measurement]


180° peeling strength Product name Substrate
SUS ABS Acrylic PC
G9951-200 14.5 14.9 15.6 18.8
  • Jerky failure


90° peeling strength Product name Substrate
G9951-200 15.6


2.Holding power at different temperatures

Test Piece Condition

Substrate:Stainless steel plate(SUS304)
Bonding area:25mm x 25mm
Bonding condition:One stroke with 2-kg roller
Backing material:25µm PET

[Left at RT for one hour and then at each temperature for 30 minutes before measurement]
[Creep length after one hour application of 1-kg load]

Creep length(mm) Product name Measurement temperature
40°C 100°C
G9951-200 0.8 1.3

3.Curved surface bending on various type of substrate

Test Piece Condition

Substrate(1):Aluminum plate 0.5mm x 20mm x 150mm
Substrate(2):ABS plate, PS plate 2mm x 25mm x 200mm
Bonding condition:One stroke with 2-kg roller
Measuring condition:50°C

[Left at RT for one day, then lifting height of the edge after the elapsed time is measured]

Lifting height(mm) Product name Substrate
G9951-200 0.0 0.0


Note on the characteristic data given - Data on the characteristics of the products described in this page based on the results of evaluations carried out by the company. This does not guarantee that the characteristics of the product conform with your usage environment. Before use, review the usage conditions based on evaluation data obtained from the equipment and substrates actually used.