Double coated tapes

Flame retardant type double coated tapes

High flame retardancy. Green tape. High flame retardancy.

  • Product name
    UT1515
  • Features
    • No solvent used at coating process. UV curable manufacturing method.
    • Can be used in environments of up to 120°C.
    • High flame retardation.
s_ico_01.gifs_ico_02.gif

Structure

Specifications

Product name UT1515
Main component Acrylic base
Carrier Nonwoven fabric
Color White
Adhesive thickness(µm) About 150
Release film thickness (µm) About 75
Bonding strength(N/20mm) *1 15
St'd size(width & length) 480mm x 50m
Warranty period from manufacturing date 12 months
  • UL certificated. UL file No: 94VTM-0 No.E63260
    *1 90° peeling strength

Ideal for bonding heat-generating parts and metals and plastics where high flame retardation is required.

1.Bonding strength on various type of substrate (90° peeling)

Test Piece condition

Tape width:20mm
Bonding condition:One stroke with 2-kg roller
Measuring condition:23°C±5°C 60%±20%RH
Peeling speed:300mm/min
Backing material:40µm aluminum foil

[Left at RT for one day before measurement]

Results

(N/20mm)

90° peeling strength Product name Substrate
SUS Glass Aluminum ABS PS PC
UT1515 15.0 11.6 10.8 14.0 13.0 12.4

2.Holding power at different temperatures

Test Piece condition

Substrate:Stainless steel plate (SUS304)
Bonding area:25mm x 25mm
Bonding condition:One stroke with 2-kg roller
Backing material:40µm aluminum foil

[Left at RT for one hour and then at each temperature for 30 minutes before measurement]
[Creep length after one-hour application of 1-kg load]

Results
Creep length (mm) Product name Measurement temperature
80°C 120°C 150°C
UT1515 0.1 0.2 0.4

caution

Note on the characteristic data given - Data on the characteristics of the products described in this page based on the results of evaluations carried out by the company. This does not guarantee that the characteristics of the product conform with your usage environment. Before use, review the usage conditions based on evaluation data obtained from the equipment and substrates actually used.