Double coated tapes

Removable type double coated tapes

Excellent reworkability without tearing.

  • Product name
    G9000R
  • Features
    • No solvent used at coating process. UV curable manufacturing method.
    • High heat resistance ; can be used in environments of up to 100°C.
    • High adhesive quality (heat resistance and weather resistance) for wide ranging applications.
    • High processability for seal cutting (half cutting).
    • Removable model: Little paste left after an extended period of use.
s_ico_01.gif

Product Lineup

Structure

Specifications

Product name G9000R
Main component Acrylic base
Carrier Nonwoven fabric
Color Translucent
Adhesive thickness(µm) About 150
Release paper thickness(µm) About 150
Bonding strength
(N/20mm) *1
15
St'd size (width & length) 500mm x 50m
Warranty period from manufacturing date 12 months
  • UL certificated. UL file No:( UL969 No.MH15431)
    *1 180° peeling strength

Ideal for bonding recycling objective parts such as backing materials of office automation equipment and televisions and vibration suppression materials.

1.Bonding strength on various type of substrate (180° peeling)

Test Piece ondition

Tape width:20mm
Bonding condition:One stroke with 2-kg roller
Measuring condition:23°C±5°C 60%±20%RH
Peeling speed:300mm/min
Backing material:25µm PET

[Left at RT for one hour before measurement]

Results

(N/20mm)

180° peeling strength Product name Substrate
SUS ABS Glass
G9000R 15.1 14.4 13.2

2.Holding power at different temperatures

Test Piece Condition

Substrate:Stainless steel plate (SUS304)
Tape bonding area:25mm x 25mm
Bonding condition:One stroke with 2-kg roller

[Left at RT for one hour and then at each temperature for 30 minutes before measurement]
[Creep length after one hour application of 1-kg load]

Results
Creep length(mm) Product name Measurement temperature
40°C 60°C 80°C 100°C
G9000R 0.2 0.2 0.3 0.4

3. Removable evaluation under each temperature by elapsed time (180° peeling)

Test Piece Condition

Substrate:ABS plate
Tape width:20mm
Bonding condition:One stroke with 2-kg roller
Measuring condition:23°C±5°C 60%±20%RH
Peeling speed:300mm/min
Backing material:25µm PET

[Left at RT for one hour and aged at a predetermined temperature for 8 weeks before measurement]

Results

(N/20mm)

Removable evaluation
(180° peeling strength)
Product name Aging condition Measurement time
Initial 1week 2weeks 4weeks 8weeks
G9000R -30°C 14.4 19.3 18.6 19.0 17.5
60°C 14.4 20.4 19.8 21.2 22.9
40°C 90%RH 14.4 17.5 19.0 20.2 20.7
  • ※ Good. (There is no paste remainder to the substrate.)
  • g9000r_chart_04.gif

caution

Note on the characteristic data given - Data on the characteristics of the products described in this page based on the results of evaluations carried out by the company. This does not guarantee that the characteristics of the product conform with your usage environment. Before use, review the usage conditions based on evaluation data obtained from the equipment and substrates actually used.