General-purpose double coated tapes

High-performance, general-purpose double coated series usable for various purposes produced employing Green tape ®.

  • Product name
    G9000/G9000W
  • Features
    • No solvent used at coating process. UV curable manufacturing method.
    • High heat resistance : can be used in environments of up to 100°C.
    • High adhesive quality (heat resistance and weather resistance) for wide ranging applications.
    • High processability for seal cutting (half cutting).
s_ico_01.gif

Product Lineup

Structure

Specifications

Product name G9000 G9000W *2
Main component Acrylic base Acrylic base
Carrier Nonwoven fabric Nonwoven fabric
Color Translucent Translucent
Adhesive thickness(µm) About 150 About 150
Release paper thickness(µm) About 150 About 150+120
Bonding strength(N/20mm) *1 14 14
St'd size(width & length) 500mm x 50m 500mm x 50m
Warranty period from manufacturing date 12 months 12 months
  • UL certificated. UL file No:( UL969 No.MH15431)
    *1 180° peeling strength
    *2 G9000W: With both side release paper.

Ideal for bonding nameplates and front panels that need to be heat resistance.

1.Bonding strength on various type of substrate (180° peeling)

Test Piece Condition

Tape width:20mm
Bonding condition:One stroke with 2-kg roller
Measuring condition:23°C±5°C 60%±20%RH
Peeling speed:300mm/min
Backing material:25µm PET

[Left at RT for one hour before measurement]

Results

(N/20mm)

180° peeling strength Product name Substrate
SUS AL ABS Acrylic PS PP PC
G9000 13.7 8.8 11.6 12.4 11.5 5.1 11.9
  • ※ PP:Jerky failure.
180° peeling strength Product name Substrate
Soft PVC Hard PVC Glass CR NR
G9000 12.6 13.2 12.9 3.4 4.0

2.Holding power at different temperatures

Test Piece Condition

Substrate:Stainless steel plate (SUS304)
Bonding area:25mm x 25mm
Bonding condition:One stroke with 2-kg roller

[Left at RT for one hour and then at each temperature for 30 minutes before measurement]
[Creep length after one hour application of 1-kg load]

Results
Creep length(mm) Product name Measurement temperature
40°C 60°C 80°C 100°C
G9000 0.2 0.3 0.3 0.6

3.Bonding strength at different temperatures (180° peeling)

Test Piece Condition

Substrate:Stainless steel plate (SUS304)
Tape width:20mm
Bonding condition:One stroke with 2-kg roller
Peeling speed:300mm/min

[Left at RT for one hour and then at each temperature for 30 minutes before measurement]

Results

(N/20mm)

180° peeling strength Product name Measurement temperature
-20°C 0°C 5°C 10°C 23°C 40°C 60°C 80°C 100°C
G9000 ※1 32.4 28.3 25.5 17.4 14.4 11.9 10.8 9.3
  • ※1:AF on backing material

4.Stable weight peeling

Test Piece Condition

Tape width:20mm
Bonding condition:One stroke with 2-kg roller
Measuring condition:23°C±5°C 60%±20%RH

[Left at RT for one hour before measurement]
[Measurement of distance peeled (mm) after application of 100-g load]

Results
Peeling distance (mm) Product name Substrate
Aging SUS AL ABS PS Acrylic PP
G9000 1hour 1.0 2.0 2.0 2.5 2.0 3.5
3hours 1.3 3.0 3.5 5.0 3.3 7.8
5hours 1.3 2.8 4.5 7.5 4.5 11.0
24hours 1.5 9.5 18.5 34.0 16.0 59.0

caution

Note on the characteristic data given - Data on the characteristics of the products described in this page based on the results of evaluations carried out by the company. This does not guarantee that the characteristics of the product conform with your usage environment. Before use, review the usage conditions based on evaluation data obtained from the equipment and substrates actually used.