Double coated tapes

Special resin base hotmelt double coated tapes

Flexible. Highly thermal conductive.

  • Product name
    D3600
  • Features
    • Fills cavities and clearances for strong bonding in hot melting processes.
    • The tape is tack-free at room temperature, enabling die-cutting without release paper.

Product Lineup

Structure

Specifications

Product name D3600
Main component Polyester base
Carrier Non-carrier
Color Translucent
Adhesive thickness(µm) About 50
Release paper thickness (µm) About 130
Bonding strength(N/20mm x 20mm) *1 2,550
St'd size(width & length) 510mm x 100m
Warranty period from manufacturing date 12 months
  • *1 Shear strength (Bonding temperature 150°C)

Application Example

Ideal for a mass-production scale adhesion process of brass plates of VTR terminals and glass epoxy base materials and nameplate parts.

Technical Data

1.Bonding strength under different temperatures (Shear strength)

Shear strength test

Test Pisce Condition

Substrate(1):Stainless steel plate (0.5mmx25mmx100mm)
Substrate(2):PC / ABS plate(4mmx25mmx100mm)
Bonding area:20mm x 20mm
Bonding condition:Temperature / 100°C to 200°C, Time / 3sec, Pressure / 0.5MPa(5kgf/cm2)
Measuring condition:23°C±5°C 60%±20%RH
Peeling speed:20mm/min

[Left at RT for one day before measurement]

Results

(N/40mm2)

Shear strength Product name Bonding temperature
100°C 110°C 120°C 130°C 140°C 150°C
D3600 1,407 1,736 2,197 2,481 2,545 2,550
Shear strength Product name Bonding temperature
160°C 170°C 180°C 190°C 200°C
D3600 2,609 2,614 2,677 2,839 3,242
d3600_chart_01.gif

2.Bonding strength at different temperature (Push out test)

Push out test
Test Piece Condition

Substrate(1):Stainless steel plate(1.0mm x 50mm x 100mm)
Substrate(2):PC,ABS plate(2mm x 38mm x 64mm)
Bonding area:20mm x 35mm / 2 pieces
Bonding condition:Temperature / 120°C to 140°C, Time / 3sec, Pressure / 0.5MPa(5kgf/cm2)
Measuring condition:23°C±5°C 60%±20%RH
Pushing speed:10mm/min

[Left at RT for one day before measurement]

Results

(N/1.4cm2)

Push out test Product name Measurement temperature
120°C 130°C 140°C
D3600 39.2 73.6 250.2

3.Impact force resistance (Drop test)

Impact force (Drop test(1)) registant test

Test Piece Condition

Substrate(1):Stainless steel plate(1.0mm x 50mm x 100mm)
Substrate(2):PC,ABS plate(2mm x 50mm x 100mm)
Bonding area:10mm x 10mm
Bonding condition:Temperature / 120°C to 140°C, Time / 3sec, Pressure / 0.5MPa(5kgf/cm2)
Measuring condition:23°C±5°C 60%±20%RH
Height:1.5m
Weight:300g

[Left at RT for one day before measurement]

Results
Impact force resistance
Drop test		 Product name Measurement temperature
120°C 130°C 140°C
D3600 17.0
8.0		 26.0
20.0		 30 or less
30 or less
  • ※ The test piece is dropped to concrete. Record the numbers when the test piece peel off.

caution

Note on the characteristic data given - Data on the characteristics of the products described in this page based on the results of evaluations carried out by the company. This does not guarantee that the characteristics of the product conform with your usage environment. Before use, review the usage conditions based on evaluation data obtained from the equipment and substrates actually used.